High silica fiberglass fabric is a kind of excellent fabric made of high temperature resistance, inorganic fiber. The content of SiO2 is more than 96% and the weight loss of ignition is less than 3%. Its softening point is closely 1700℃ and it can be used under 1000℃ situation for a long time.
Application:
It is used for the rocket, the missile, the thermal insulation of spacecrafts as ablative materials, high temperature-proof materials and high temperature-resistant insulation materials
Product Characteristics:
Good chemical stability.
Good insulating property.
Good high-temperature resistance.
Good acid resistance and erode resistance.
Low shrinkage and thermal conductive.
Product Specifications:
|
Item |
BMT240 |
BMT340 |
BMT520 |
BMT600 |
BMT1100 |
||
|
Thickness (mm) |
0.26±0.026 |
0.4±0.04 |
0.65±0.065 |
0.75±0.075 |
1.3±0.13 |
||
|
Weight (g/m2) |
240±20 |
340±30 |
520±50 |
600±60 |
1050±100 |
||
|
Width (cm) |
80~200 |
80~200 |
80~200 |
80~200 |
80~200 |
||
|
SiO2 contents(%) |
≥96 |
≥96 |
≥96 |
≥96 |
≥96 |
||
|
Breaking Strength (N/25*100mm) |
Warp |
≥290 |
≥400 |
≥600 |
≥700 |
≥1200 |
|
|
Weft |
≥190 |
≥300 |
≥500 |
≥600 |
≥800 |
||
|
Fabric Structure |
Plain |
Satin |
Satin |
Satin |
Satin |
||
|
Treatment |
Preshrunk, coating with PU / silicone / aluminum foil / vermiculite / PTFE. Made as customers’ requests. |
||||||
Note: It has two kinds of structure, plain weave and satin weave. The thickness is 0.1 to 1.5mm.
Storage:
High Silica Fiberglass Rope/ wick should be stored in its original packaging in a dry and cool place. Best conditions are at temperatures from 15 to 35°C and humidity between 35 and 65%. To ensure safety and avoid damage to the product.
Support line / whatsapp/ wechat: +86 13882113739