Silica Fiberglass Fabric


AddTime: 2022-08-01 Print Add to Favorites Send Email: liyibin@169chem.net
Silica Fiberglass Fabric is a kind of excellent high temperature resistance fabric made of inorganic high silica fiber. The content of SiO2 is more than 96% and weight loss of ignition is less than 4% after treatment. Its softening point is closely 1700℃ and it can be used under 1000℃ situation for a long time.

Category: Fabric

Tag:silicafiberglassfabric

Hit: 70

Silica Fiberglass Fabric is a kind of excellent high temperature resistance fabric made of inorganic high silica fiber. The content of SiO2 is more than 96% and weight loss of ignition is less than 4% after treatment. Its softening point is closely 1700℃ and it can be used under 1000℃ situation for a long time.

Silica Fiberglass Fabric is a kind of excellent high temperature resistance fabric made of inorganic high silica fiber. The content of SiO2 is more than 96% and weight loss of ignition is less than 4% after treatment. Its softening point is closely 1700℃and it can be used under 1000℃ situation for a long time.

Silica fabric can be fabricated into many forms to withstand high temperatures continuously and protect personnel and equipment in severe environments, such as and thermal insulation and ablative materials of spacecrafts rocket, welding blankets, welding drop cloths, welding curtains, stress relief blankets, flame protective screens/covers, furnace curtains, insulation  shielding, emergency fire blankets and cable tray wraps, etc. High silica Fabrics are high temperature resistance fabrics extensively used for insulation and protection applications in the Aerospace, Power Generation, Shipbuilding, Refinery, Ship Repair and Metal Processing industries etc.

Product Applications:

-- Used as ablative materials.

-- Protect against hot work fires.

-- Protect equipment & personnel in toughest welding.

-- Protect from molten metal splash.

-- Used to wrap pipelines cable tray.

-- Used as emergency fire blankets.

-- Used to filter hot gas dust and air purification.

Product Characteristics:

● Resists penetration of weld “Slag”. 

● Excellent insulating properties.

● Fireproof and ablation resistance.

● Easy sewn and fabricated.

● High flexibility and high strength.

● Good acid resistance and erode resistance.

● Low thermal shrinkage.

● Non-asbestos or ceramic fibers.


Product Specifications:

Note: Other specifications could be made as requests.

Item

HSWT260

HSWT280

HSWT340

HSWT1584

HSWT1586

Thickness (mm)

0.26±0.026

0.28±0.028

0.4±0.04

0.76±0.076

1.3±0.13

Weight (g/m2)

220±20

240±20

340±30

630±60

1050±100

Width (cm)

80~200

80~200

80~200

80~200

80~200

SiO2 content (%)

≥96

≥96

≥96

≥96

≥96

Breaking Strength (N/25*100mm)

Warp

≥290

≥290

≥400

≥400

≥700

Weft

≥190

≥190

≥300

≥300

≥600

Fabric Structure

Plain

Plain

Satin

Satin

Satin

Treatment

Made as customers’ requests: Preshrunk, coating with PU / silicone / aluminum foil / vermiculite / PTFE, acrylic.

Note: Other specifications could be made as requests.

Silica fabrics cannot predict all of the potential applications for which customers may attempt to use the silica products. Silica products will have varying degrees of effectiveness for each potential application depending on the maximum temperature attained, the length of use, and the amount of temperature fluctuation. If the customer has any questions regarding the use of Silica Products in a particular application, please contact us and we will provide a sample of the Silica Products for testing. This product is not warranted against injuries or damages of any kind caused by uses for which this product was not designed, intended or tested by us.

Storage:

High Silica Fabric should be stored in its original packaging in a dry and cool place. Best conditions are at temperatures from 15 to 35°C and humidity between 35 and 65%. If no special requirements, it should be stored in cool and dry place. Don’t open the package before using to prevent absorbing moisture.

To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high, when the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.